Wironit® LA 1000 g

• Wironit^® LA – wide range of indications for reliable application in the partial denture and combination technique

• Controlled carbon content and the addition of tantalum ensure excellent laser welding properties even in extreme cases

• Low thermal conductivity means high wearing comfort for the patient

• Thanks to the high elongation of fracture, clasps can be activated without any problem

• Biocompatible and corrosion-resistant

• Item name

  Wironit® LA
• Iso type ISO22674

  5
• Casting temperature

  1450 °C
• Vickershardness

  365 HV10
• Product description

  Cobalt-Chromium partial denture alloy
• Composition

  Co 63,5 · Cr 29,0 · Mo 5,5 · Si 1,2 · C · Mn · N · Ta
• Liquidustemp.

  1390 °C
• Solidustemp

  1260 °C
• Density g/cm³

  8,2 g/cm³
• Preheat temp. to

  1050 °C
• Preheat temp. from

  950 °C
• Color code

  8
• Base metall

  Cobalt
• Content/amount

  1000 g pack
• Yield strength

  690 MPa
• Tensile strength

  890 MPa
• Elongation at break

  9 %
• Elastic modul

  240 GPa